Petrothene® GA623119
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 78EDG0_PetrotheneGA623119.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene GA623119 is a hexene LLDPE copolymer selected by customers for applications that require high clarity and good stiffness combined with low COF. It does not contain slip or antiblock additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D638 | ||
| 1% secant, MD : 25 µm, cast film | 271 | MPa | ASTM D638 |
| 1% sectioning, MD : 51 µm, cast film | 252 | MPa | ASTM D638 |
| 1% secant, TD : 25 µm, cast film | 290 | MPa | ASTM D638 |
| 1% sectioning, TD : 51 µm, cast film | 285 | MPa | ASTM D638 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 28.2 | MPa | ASTM D882 |
| MD : fracture, 51 µm, extruded film | 37.2 | MPa | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 29.0 | MPa | ASTM D882 |
| TD : fracture, 51 µm, extruded film | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 500 | % | ASTM D882 |
| MD : fracture, 51 µm, extruded film | 740 | % | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 530 | % | ASTM D882 |
| TD : fracture, 51 µm, extruded film | 840 | % | ASTM D882 |
| Dart Drop Impact | |||
| 25 µm, cast film | 140 | g | ASTM D1709 |
| 51 µm, cast film | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, cast film | 330 | g | ASTM D1922 |
| MD : 51 µm, cast film | 540 890 | g | ASTM D1922 |
| TD : 25 µm, cast film | 540 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 25.4 µm, cast film | 90 | ASTM D2457 | |
| 50.8 µm, cast film | 85 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25.4 µm, cast film | 2.4 | % | ASTM D1003 |
| 50.8 µm, cast film | 5.4 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K4038 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Borlink™ LE4201EHV | Borealis AG | PE, Unspecified | Borlink™ |
| AMPLIFY™ GR 380 | The Dow Chemical Company | MAH-g | AMPLIFY™ GR |
| Dryflex® V 60A101 | ELASTO | TPV | Dryflex® |
| POLYfill PPH GF5020 PD2 | Polykemi AB | PP Homopolymer | POLYfill |