Jamplast JPPCABS10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 77RGA8_Jamplast-JPPCABS10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPPCABS10 engineering resin is a 10% glass reinforced resin designed to provide excellent processability, high heat resistance, and practical toughness. JPPCABS10 engineering resin has been used in automotive interior trim applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 48.7 | MPa | |
| Break | 50.4 | MPa | |
| Tensile Elongation 2(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3650 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 98.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3 | ASTM D256 | ||
| -29°C, 3.18 mm | 80 | J/m | |
| 23°C, 3.18 mm | 230 | J/m | |
| Instrumented Dart Impact 4 | ASTM D3763 | ||
| -29°C, 3.18 mm, Total Energy | 5.65 | J | |
| 23°C, 3.18 mm, Peak Energy | 12.4 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 121 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 127 | °C | |
| CLTE - Flow (-40 to 82°C) | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | 0.25 mm Notch Depth |
| 4 . | 3.39 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® GF-600S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Daelim Po1y® LA-25 | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Plexiglas® V825NA | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Sylvin 9077-85 Grey 9331 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ PC1000R resin | SABIC Innovative Plastics | PC | LEXAN™ |