Latigray 80-03 CWG/850
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigray |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 77NlFV_Latigray-80-03-CWG-850.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Radiopaque compound based on Polyphenylene Sulphide (PPS). Metallic filler. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 5.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.90 | % | |
| Flow : 2.00 mm | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 14000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.1 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 3(23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 4(23°C) | 50 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 275 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Half Value Thickness | Internal Method | ||
| -- 5 | 680.0 | µm | |
| -- 6 | 520.0 | µm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 to 140 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 80x10x4 mm |
| 3 . | 80x10x4 mm |
| 4 . | 63.5x12.7x3.2 mm |
| 5 . | 120 kV |
| 6 . | 80 kV |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SR257M | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| Titacon® GF925 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| AMTOPP TE25 | Inteplast Group | PP, Unspecified | AMTOPP |
| Hostacom HRG 328T NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |
| HiFormer® Liquid Masterbatches | Clariant Corporation | TP, Unspecified | HiFormer® |