LNP™ VERTON™ MV007SUP compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 77CsQn_LNP-VERTON-MV007SUP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON MV007SUP is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. Also known as: LNP* VERTON* Compound PP MFX7007HSUV-GY03485 Product reorder name: MV007SUP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.20 to 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7700 | MPa | ISO 178 |
| Flexural Stress | 162 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 162 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 160 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 221 to 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 181 HI | RTP Company | PP Copolymer | RTP |
| Fainplast PVC PK 1080 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Ferro PP NPP00GX05GY | Ferro Corporation | PP Copolymer | Ferro PP |
| FRIANYL® A3 GF20 V0XI | Nilit Plastics | Nylon 66 | FRIANYL® |
| omay® SC42B | Suzhou OMAY Optical Materials Co., Ltd | Film, PP | omay® |