PRL PPX-GP1
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7787Bl_PRL-PPX-GP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-GP1 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 4.0 to 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.18 mm | 0.50 to 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 55.2 | MPa | |
| Break, 3.18 mm | 48.3 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 8.0 | % | |
| Break, 3.18 mm | 30 | % | |
| Flexural Modulus (3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1 |
| Notched Izod Impact | |||
| -40°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 210 | J/m | ASTM D256 |
| -30°C | 4.2 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 129 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 121 | °C | |
| Vicat Softening Temperature | 146 | °C | ASTM D1525 1 |
| RTI Elec (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 to 299 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 271 to 310 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIF4569 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TECHNYL® A 218G V33 BLACK 34N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| ESPOLEX WT502 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Jackdaw PC DX10BK | Jackdaw Polymers | PC | Jackdaw PC |
| LNP™ THERMOCOMP™ MX99432 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |