High-density, ceramic bead-filled epoxy system for maximum wear and abrasion resistance in high-temperature applications

Intended Use:

Repair scrubbers, ash handling systems, pipe elbows, screens, and chutes; recontour chippers, bins, hoppers, bunkers, separators, diester tables; protect exhausters, chutes, launderers, housing fans, crushers, and breakers.

Product Features:

Provides up to 30% better abrasion resistance than conventional wear compounds

Unmatched resistance to acids, bases, salts, and solvents

Services temperatures to 450°F

Excellent adhesion to metal, ceramic, and concrete

General Information
Filler / Reinforcement	Ceramic bead packing
Features	High density Solvent resistance Good wear resistance Good adhesion alkali resistance Good wear resistance acid resistance
Uses	Repair Materials
Appearance	Grey

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.94	g/cm³
Specific Volume	0.517	cm³/g
Solid content- by Volume	100	%

Additional Information	Nominal Value	Unit	Test Method
Temperature Resistance
Dry	232	°C
Wet	66	°C
Tensile Shear Adhesion	15.9	MPa	ASTM D1002

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	0.10	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	87		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	31.7	MPa
Flexural Strength	56.7	MPa	ASTM D790
Compressive Strength	91.0	MPa	ASTM D695

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	4.9E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value		Test Method
Dielectric Constant	38.0		ASTM D150

Thermoset	Nominal Value	Unit	Test Method
Thermoset Components
Component a	Mixing ratio by weight: 14 Mixing ratio by capacity: 6.0
Component B	Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0
Pot Life (24°C)	120	min

Additional Information	Nominal Value	Unit	Test Method
Cured 7 days @ 75°F

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU F595FCOO	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
Sylvin 8334-60FU White 1510	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LEXAN™ ML2910 resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™
Karina NATURAL PVC COMPOUND 70900-25/ 1-E-IS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
PEEK-OPTIMA® LT3	Invibio Inc.	PEEK	PEEK-OPTIMA®