VITAMIDE® TS10NT6164
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 74RoMp_VITAMIDE-TS10NT6164.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® TS10NT6164 is a Polyamide 66/6 Copolymer (Nylon 66/6) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Break | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 5.00 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | No Break | ASTM D256 | |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact Strength | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 205 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 240 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 26 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 600 | V | IEC 60112 |
| -- 3 | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G30 HS UV PRTA011 NR395 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Badamid® B70 GK30 FR HF | Bada AG | Nylon 6 | Badamid® |
| ELASTOSIL® R plus 4000/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Grilamid® LV-50H FWA nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Plaslube® J-50/30/TF/15 | Techmer Engineered Solutions | PC | Plaslube® |