Nycast 6PA-MoS2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Cast Nylons Ltd. |
| Trademark: | Nycast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 741gih_Nycast-6PA-MoS2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYCAST 6PA-MoS2 is a popular choice as a dry lubricant-filled bearing material. Manufactured to be a more crystalline product with improved wear resistance, NYCAST 6PA-MoS2 also offers improved compressive strength. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 to 1.17 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.50 to 0.60 | % | |
| Saturation | 5.0 to 6.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 to 125 | ASTM D785 | |
| Durometer Hardness (Shore D) | 78 to 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 to 3790 | MPa | ASTM D638 |
| Tensile Strength | 68.9 to 93.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 to 55 | % | ASTM D638 |
| Flexural Modulus | 2900 to 3450 | MPa | ASTM D790 |
| Flexural Strength | 107 to 121 | MPa | ASTM D790 |
| Compressive Modulus | 2240 to 2760 | MPa | ASTM D695 |
| Compressive Strength | 93.1 to 110 | MPa | ASTM D695 |
| Shear Strength | 68.9 to 75.8 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.22 | ASTM D1894 | |
| Deformation Under Load | 0.500 to 2.50 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 to 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 204 to 221 | °C | |
| 1.8 MPa, Unannealed | 93.3 to 204 | °C | |
| Continuous Use Temperature | 110 | °C | ASTM D794 |
| Melting Temperature | 227 to 238 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Service Temperature - Intermittent | 166 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 to 24 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.70 | ||
| 1 kHz | 3.70 | ||
| 100 kHz | 3.70 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204A | RTP Company | Nylon 6 | RTP |
| Reny® F34S | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Mirakutoran® TPU E890PBOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Braskem PP RP 141 | Braskem | PP Random Copolymer | Braskem PP |
| Jampilen RP129K | Jam Polypropylene Company | PP Terpolymer | Jampilen |