Celanex® 5214
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 72aY2T_Celanex5214.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 5214 is a 15% glass reinforced, high gloss, flame retardant polyester. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 7100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS F5451G10 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| TIPELIN® 7300B | MOL Petrochemicals Co. Ltd. | HDPE | TIPELIN® |
| ASTALAC™ ABS M140 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Edgetek™ COC BLEND-15GF Natural | PolyOne Corporation | COC | Edgetek™ |
| LNP™ THERMOTUF™ VF004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |