EPO-TEK® 730 Black
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 72GkuB_EPO-TEK-730-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, room temperature curing, general and structural grade epoxy resin. It can be used for adhesive and sealing applications in medical, x-ray device, filtration, opto-electronics, and PCB industries. It is a thixotropic, black version of EPO-TEK® 730. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 364 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 150 | °C | |
| Intermittent | -55 to 250 | °C | |
| Storage Modulus (23°C) | 762 | MPa | |
| Thixotropic Index | 2.10 | ||
| Weight Loss on Heating | |||
| 200°C | 1.4 | % | |
| 250°C | 2.2 | % | |
| 300°C | 4.2 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 55.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 8.2E-5 | cm/cm/°C | |
| -- 3 | 2.5E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance | |||
| 480 nm | < 10.0 | % | |
| 980 nm | < 25.0 | % | |
| 1550 nm | < 45.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Black | ||
| -- 5 | Tan | ||
| Density | |||
| Part B | 0.938 | g/cm³ | |
| Part A | 1.12 | g/cm³ | |
| Viscosity 6(23°C) | 80 to 120 | Pa·s | |
| Curing Time (80°C) | 2.0 | hr | |
| Pot Life | 60 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.50 | ||
| Volume Resistivity (23°C) | > 1.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.024 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | 2.5 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® A2 500450M | ELASTO | SEBS | Mediprene® |
| K-vinyl 20 A 74 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| INNOPOL® PP CS 2-5000 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| Plaslube® ABS/PBT 1500 | Techmer Engineered Solutions | ABS+PBT | Plaslube® |
| Sylvin 9993-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |