LNP™ THERMOCOMP™ VF008A compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 71fXuV_LNP-THERMOCOMP-VF008A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP VF008A is a compound based on High Impact Nylon 66 containing 40% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PDX-83363 Product reorder name: VF008A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | Internal Method |
| Water Absorption (24 hr, 50% RH) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 158 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 8270 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 227 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5(23°C) | 190 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1000 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 249 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 293 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E180 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SUMIKAEXCEL® PES 4101GL30 | Sumitomo Chemical Co., Ltd. | PESU | SUMIKAEXCEL® PES |
| YUPLENE® BX36A | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| SCHULABLEND® (ABS/PA) M/MK 6101 GF8 U | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |
| LEXAN™ FST3403 resin | SABIC Innovative Plastics | PC | LEXAN™ |