SINOF DH-F22I
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SINOF HI-TECH MATERIAL CO. LTD |
| Trademark: | SINOF |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 71cDCA_SINOF-DH-F22I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DH-F22I is one kind of pellet PVDF with lower melting viscosity and suitable for making various PVDF products through injection. Products made from DH-F22I have a wide range of service temperature (-50°C to 150°C) |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 16 to 24 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | < 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 76 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C | > 40.0 | MPa | |
| 23°C | > 25.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C | 5.0 to 10 | % | |
| Break, 23°C | > 20 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 4 | 168 to 173 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2320SN | Ginar Technology Co., LTD. | Nylon 66/6 | Mapex |
| Ultraform® N 2320 C BK110 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Nylene® 132-250 | Custom Resins Group | Nylon 66 | Nylene® |
| Fainplast PVC R 220/R | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| LUVOCOM® 1-8172 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |