CoolPoly® D5502
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 71Q5M2_CoolPoly-D5502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 | % | ASTM D955 |
| Transverse flow | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 0.64 | % | ISO 527-2 |
| Flexural Modulus | 10200 | MPa | ISO 178 |
| Flexural Stress | 101 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 3.7 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Specific Heat | 1000 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 1.5 | W/m/K | ASTM C177 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM E1461.The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with ASTM D551.The value listed as Specific Heat ASTM C351, was tested in accordance with ASTM E1461.Thermal Diffusivity, ASTM E1461: 0.00843 cm²/sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Dew Point | -40.0 | °C | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 330 - 360 | °C | |
| Middle Temperature | 340 - 370 | °C | |
| Front Temperature | 345 - 380 | °C | |
| Nozzle Temperature | 350 - 382 | °C | |
| Processing (Melt) Temp | 349 - 393 | °C | |
| Mold Temperature | 93.0 - 177 | °C | |
| Injection Pressure | 35.0 - 70.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 7.00 - 35.0 | MPa | |
| Back Pressure | 0.00 - 0.350 | MPa | |
| Screw Speed | 75 - 150 | rpm | |
| Cushion | 10.0 - 13.0 | mm | |
| Screw Compression Ratio | 3.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 AR 15 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Vital-Line SHM3600G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| DINALON® PA 6 | Grupo Repol | Nylon 6 | DINALON® |
| LUVOCOM® 1-0865 VP | LEHVOSS Group | Nylon 66 | LUVOCOM® |
| Hifax CA 1110 G4 C11306 | LyondellBasell Industries | PP Copolymer | Hifax |