KumhoSunny PC HCG2510FR
| Category: | PC , Polycarbonate |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 70yLAb_KumhoSunny-PC-HCG2510FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HCG2510FR is 10%GF flame retardant PC resin. It has high rigidity and super shape resistance property. HCG2510FR is mainly used in electron & electric parts, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 3500 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 142 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 275 to 285 | °C | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Firepel® K130-LCS-00 | AOC, L.L.C. | Polyester Alloy | Firepel® |
| HAIPLEN H50 C4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Huafon JF-P-8875D / JF-I-8918D (midsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| INLUBE PESCF30TF15 | Infinity LTL Engineered Compounds | PESU | INLUBE |
| POLIMAXX 2511HXGA5 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |