Starex WX-9310UV
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 70WUwE_Starex-WX-9310UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Heat resistant ASA that is applied to the interior/exterior material of automobile |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.45 | % | ASTM D955 |
| Across Flow : 3.20 mm | 0.50 | % | ASTM D955 |
| Across Flow : 3.20 mm | 0.45 | % | ISO 2577 |
| Flow : 3.20 mm | 0.50 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 105 | ASTM D785 | |
| R-Scale | 106 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 44.0 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2/50 |
| Break 3 | 36.0 | MPa | ASTM D638 |
| Break | 37.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 12 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2200 | MPa | ASTM D790 |
| -- 6 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 67.0 | MPa | ASTM D790 |
| -- 8 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 180 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 88 | J/m | ASTM D256 |
| 23°C 10 | 16 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 97.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 96.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 80.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ISO 306/B50 |
| -- | 103 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 124790 B | RTP Company | PLA | RTP |
| STYRON™ H9152T | Trinseo | PS (HIPS) | STYRON™ |
| Bergamid™ B70 G33 U GR258 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Karina WHITE PVC COMPOUND 807D10/121-D-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® AKV 35 CX H2.0 900876 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |