Lucon® CP6059F
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6zvkho_LuconCP6059F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Electrostatic Dissipation (1.0E+04 ~ 1.0E+07 ohm) Halogen Free Flame Retandant Low Liquid Particle Counts Application HDD parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 - 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 8.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3330 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 93.0 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+7 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+4 - 1.0E+8 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-1 | UL 94 | |
| 3.0 mm | V-1 | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Electrostatic Decay 5 | sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 250 - 265 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Mold Temperature | 50 - 80 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 1000V to <100V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Provista™ Copolymer ST | Eastman Chemical Company | Polyester, TP | Provista™ |
| Spectar™ Sheet | Spartech Plastics | Copolyester | Spectar™ |
| APEX® 586 | Teknor Apex Company | PVC, Flexible | APEX® |
| Ecobarrier® 2618PE | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |
| Elastollan® 688A10N Film | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |