OxyShield® 1545
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | OxyShield® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6zTAn0_OxyShield-1545.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Oxyshield®1545 is a 0.59 mil (15 micron) biaxially oriented nylon 6 film coated on one side with PVdC. The coating is applied without the need for a primer layer and so presents superior coating adhesion and laminating adhesion to other films. Medium oxygen and moisture vapor barrier and superior clarity are properties well suited for packaging applications requiring excellent mechanical strength and long shelf life. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With metal-dynamic, extrusion coating | 0.55 | ASTM D1894 | |
| With Metal-Dynamic | 0.30 | ASTM D1894 | |
| With metal-static | 0.40 | ASTM D1894 | |
| With metal-static, extrusion coating | 1.3 | ASTM D1894 | |
| With self-dynamics | 0.65 | ASTM D1894 | |
| With Self-Static | 1.1 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 15 µm | 2320 | MPa | ASTM D882 |
| TD : 15 µm | 2150 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 15 µm | 248 | MPa | ASTM D882 |
| TD : Break, 15 µm | 248 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 87 | % | ASTM D882 |
| TD : Break, 15 µm | 87 | % | ASTM D882 |
| Oxygen Permeability (23°C, 15 µm, 65% RH) | 0.35 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (15 µm, 38°C, 100% RH) | 12 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (15.0 µm) | < 5.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield: 40800 in²/lbTensile Strength @ Break, ASTM D 882, MD: 34000 to 38000 psiTensile Strength @ Break, ASTM D 882, TD: 34000 to 38000 psiElongation @ Break, ASTM 882, MD: 75 to 100%Elongation @ Break, ASTM 882, TD: 75 to 100%Secant Modulus, ASTM D 882, MD: 300000 to 375000 psiSecant Modulus, ASTM D 882, TD: 275000 to 350000 psiGraves Tear (initial), ASTM D 1004, MD: 1100 to1400 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 to1400 g/milCoefficient of Friction, ASTM D 1894: 0.6 to 0.7 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.9 to 1.3 vs Itself-StaticCoefficient of Friction, ASTM D 1894: 0.2 to 0.4 vs Metal-DynamicCoefficient of Friction, ASTM D 1894: 0.3 to 0.5 vs Metal-StaticCoefficient of Friction, ASTM D 1894, Extrusion Coated: 0.4 to 0.7 vs Metal-DynamicCoefficient of Friction, ASTM D 1894, Extrusion Coated: 0.8 to 1.8 vs Metal-StaticDimensional Stability, ASTM D1204, MD, 320°F, 5min: < 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: <1.5% shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ G80A-32U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Trilliant™ HC HC6010-8001 WT | PolyOne Corporation | Nylon 6 | Trilliant™ HC |
| BCC Resins BC 7009-2 | BCC Products Inc. | Epoxy | BCC Resins |
| CALP 1620G-1 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Dow ENDURANCE™ HFDA-0801 BK EHV | The Dow Chemical Company | TP, Unspecified | Dow ENDURANCE™ |