Iupilon® MB1700
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xpvXZ_Iupilon-MB1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® MB1700 is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® MB1700 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 61.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.9 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 55 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 92.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 82.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | HB | ||
| 0.600 mm | V-2 | ||
| 0.810 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 210 to 250 | °C | |
| Middle Temperature | 220 to 260 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Nozzle Temperature | 230 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 30 to 50 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA ABS 4152 | MBA Polymers | ABS | MBA ABS |
| RTP VLF 80209 EM HS | RTP Company | Nylon 66 | RTP |
| Torayca® TLP1060 | Toray Resin Company | Nylon 6 | Torayca® |
| Karina NATURAL PVC COMPOUND -E TR-75701-25/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND -E 854-10/150-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |