Vi-Chem PVC V143-70I
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Vi-Chem PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xVdQU_Vi-Chem-PVC-V143-70I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vi-Chem PVC V143-70I is a Polyvinyl Chloride material. It is available in North America. Typical application of Vi-Chem PVC V143-70I: Automotive |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792A, ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 63 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield 1 | 9.90 | MPa | ISO 527-2/500 |
| -- | 9.90 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638, ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | |||
| -- 2 | 30.0 | kN/m | ASTM D624 |
| -- 3 | 30 | kN/m | ISO 34-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (85°C, 1000 hr) | 2.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (85°C, 1000 hr) | -8.0 | % | ISO 188 |
| Change in Mass in Air (85.0°C, 1000 hr) | 1.2 | % | ISO 188 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold Flexibility 4(-34°C) | No Cracks |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | Self Extinguish | ISO 3795 | |
| Fogging 5 | 80 | % | SAE J1756 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Contact Migration Staining 6 | Pass | ||
| Odor 7 | Rating 2 | ||
| Paint Staining 8 | Pass | ||
| Xenon Arc - Delta E 9 | 0.390 | SAE J1885 |
| Note Message | |
|---|---|
| 1 . | Type 5A |
| 2 . | Die C |
| 3 . | Method Ba, Angle (Unnicked) |
| 4 . | 19 to 20 mm Mandrel, FLTM BN 102-01 |
| 5 . | 3 hr, 100°C heating, 21C cooling |
| 6 . | FLTM BN 003-01 |
| 7 . | FLTM BO 131-01/SAE J1351 |
| 8 . | FLTM BP 153-01, Procedure A |
| 9 . | 601.6 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chiao Fu PBT PBT312B30 BK | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| Garaflex™ G 7765-A5R NATURAL | AlphaGary | TPE | Garaflex™ G |
| Huafon JF-S-HS90 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina WHITE PVC COMPOUND 700D10/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8240-98FU White 1512 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |