NORYL GTX™ GTX678 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6xEPk5_NORYLGTXGTX678resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be electro-statically painted or powder coated without the need for a conductive primer. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 7.8 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 - 1.5 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2900 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 58.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 52.0 | MPa | ASTM D638 |
| Fracture | 52.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Fracture 5 | 12 | % | ASTM D638 |
| Fracture | 12 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2600 | MPa | ASTM D790 |
| -- 7 | 2600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 70 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 195 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 191 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 198 | °C | ASTM D1525 13 |
| -- | 197 | °C | ISO 306/B50 |
| -- | 195 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1400 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-1 | UL 94 | |
| 2.00 mm, Testing by SABIC | V-0 5VB 5VA | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 260 - 299 | °C | |
| Middle Temperature | 266 - 299 | °C | |
| Front Temperature | 271 - 299 | °C | |
| Nozzle Temperature | 277 - 299 | °C | |
| Processing (Melt) Temp | 277 - 299 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 245 - 260 | °C | |
| Cylinder Zone 2 Temp. | 245 - 260 | °C | |
| Cylinder Zone 3 Temp. | 245 - 260 | °C | |
| Cylinder Zone 4 Temp. | 245 - 260 | °C | |
| Adapter Temperature | 245 - 260 | °C | |
| Melt Temperature | 245 - 260 | °C | |
| Die Temperature | 245 - 260 | °C | |
| Calibration Temp, First | 35.0 - 75.0 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 24 hrsWater Bath Temperature: 35 - 50 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 C | RTP Company | Nylon 11 | RTP |
| RELENE® 45GP004 | Reliance Industries Limited | HDPE | RELENE® |
| Adell PP EA-38 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Exxtral™ Performance Polyolefin CNW010 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Iupiace® GV10 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |