Petrothene® KR92828
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6vmaws_Petrothene-KR92828.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE KR 92828 is a high molecular weight, high density polyethylene-based compound designed for use in jacketing, conduit or wire insulation. KR 92828 contains a carbon black content of 2.5%. Antioxidant has been added to ensure thermal stability during processing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.17 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal) | 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant | 531 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 19.3 | MPa | ASTM D638 |
| Fracture | 31.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 758 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.0 | °C | ASTM D746 |
| CLTE - Flow | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-4 | ASTM D150 |
| Additional Information |
|---|
| The value listed as Dielectric Constant, ASTM D150, was tested in accordance with ASTM D1531.The value listed as Dissipation Factor, ASTM D150, was tested in accordance with ASTM D1531.Absorption Coefficient, ASTM D3349: 440 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 - 163 | °C | |
| Cylinder Zone 2 Temp. | 177 - 204 | °C | |
| Cylinder Zone 3 Temp. | 191 - 204 | °C | |
| Cylinder Zone 4 Temp. | 238 - 260 | °C | |
| Adapter Temperature | 246 - 260 | °C | |
| Melt Temperature | 246 - 260 | °C | |
| Die Temperature | 246 - 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® E5000 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Syncure™ System S117FH | PolyOne Corporation | XLPE | Syncure™ |
| K-Resin® SBC KR03NW | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |
| TECACOMP® PEEK 450 CF30 black 3198 | Ensinger GmbH | PEEK | TECACOMP® |
| LNP™ FARADEX™ MS003 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ FARADEX™ |