Lupolen 2427 K
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6vhVPg_Lupolen-2427-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupolen 2427 K is an additivated, low density polyethylene. It contains an antioxidant, slip and anti-blocking agent. It is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 260 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 11.0 | MPa | ISO 527-2 |
| Coefficient of Friction (Blown Film) | < 0.20 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 15 to 40 µm | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, Blown Film | 19.0 | MPa | |
| TD : 50 µm, Blown Film | 16.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 300 | % | |
| TD : Break, 50 µm, Blown Film | 600 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 100 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20°, 50.0 µm, Blown Film | > 50 | ||
| 60°, 50.0 µm, Blown Film | > 100 | ||
| Haze (50.0 µm, Blown Film) | < 9.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy 1(50.0 µm) | 35.0 | J/cm | DIN 53373 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME GPPS SC205 | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Unichem 81-001 | Colorite Polymers | PVC, Unspecified | Unichem |
| Fainplast PVC RKS 310/K1 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Karina IVORY PVC COMPOUND 75920-35/1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plasmer 2055N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |