Starex HF-0680 U
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6uSFce_StarexHF0680U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex HF-0680 U is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.2 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 108 | ASTM D785 | |
| R scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 44.1 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2160 | MPa | ASTM D790 |
| -- 3 | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 60.8 | MPa | ASTM D790 |
| -- 5 | 59.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 21 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 6.35 mm | 230 | J/m | ASTM D256 |
| -30°C 7 | 19 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 160 - 180 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 49.0 - 147 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4mm |
| 7 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP240T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| YUPLENE® R370F | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| FLEXOMER™ ETS-9066 NT 7 | The Dow Chemical Company | VLDPE | FLEXOMER™ |
| Keltan® 9950C | LANXESS Buna GmbH | EPDM | Keltan® |
| EnviroTPE 80A | West Michigan Compounding | TPE | EnviroTPE |