Diaterm® A27 GK20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DTR S.r.l. (Develop Thermoplastic Resins) |
| Trademark: | Diaterm® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6uAVgV_Diaterm-A27-GK20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diaterm®A27 GK20 is a polyamide 6 (nylon 6) material, which contains a 20% glass fiber reinforced material. This product is available in Europe,. Diaterm®The main features of A27 GK20 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 3900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 180 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 185 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Water Absorption, DIN 53714, 23°C, 50% RH: 2.5%Burning Rate, DIN 75200: <100mm/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 5060 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| NYLAFORCE® B 50 Z SCHWARZ | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | NYLAFORCE® |
| Deltech PS Grade 120 | Deltech Polymers Corporation | PS (GPPS) | Deltech PS |
| Hifax X M1 T05 | LyondellBasell Industries | PP Copolymer | Hifax |
| IDI SMC S30 (Glass Content 25%) | IDI Composites International | TS, Unspecified | IDI SMC |