LEXAN™ OQ1028 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6tgIHf_.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Optical quality, high purity PC resin for CD/DVD and BD applications at short cycle times |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/1.2 kg) | 9.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | |||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2350 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 60.0 | MPa | ASTM D638 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 6 | > 40 | % | ASTM D638 |
| Fracture | > 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 2300 | MPa | ASTM D790 |
| -- 8 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 10 | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 11 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 132 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 132 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 122 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ASTM D1525, ISO 306/B50 10 14 |
| -- | 140 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.010 | IEC 60250 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance (2540 µm) | > 90.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 0.70 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 320 - 340 | °C | |
| Front Temperature | 350 - 380 | °C | |
| Nozzle Temperature | 340 - 370 | °C | |
| Processing (Melt) Temp | 340 - 370 | °C | |
| Mold Temperature | 75.0 - 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 |
| 11 . | 80*10*3 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC5-4420 | Spartech Polycom | PP Copolymer | Spartech |
| Nypol® PA A3 G25 FR HS NTLA010 NR350 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| CALP 4006G-2A | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Hanwha Total PP CH72W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Idemitsu PS IT43 | Idemitsu PS | PS (GPPS) | Idemitsu PS |