CP PRYME® ABS A100HIE-84
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6tBI9Z_CPPRYMEABSA100HIE84.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Prime ABS, High Impact, Extrusion Grade, Natural |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2030 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 39.3 | MPa | ASTM D638 |
| Fracture | 29.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.1 | % | ASTM D638 |
| Fracture | 32 | % | ASTM D638 |
| Flexural Modulus (50.0 mm Span) | 2100 | MPa | ASTM D790 |
| Flexural Strength (Yield, 50.0 mm Span) | 63.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 430 | J/m | ASTM D256 |
| Instrumented Dart Impact | 33.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 93.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 - 93 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 171 - 199 | °C | |
| Cylinder Zone 2 Temp. | 182 - 221 | °C | |
| Cylinder Zone 3 Temp. | 188 - 227 | °C | |
| Cylinder Zone 4 Temp. | 199 - 238 | °C | |
| Adapter Temperature | 204 - 249 | °C | |
| Melt Temperature | 216 - 260 | °C | |
| Die Temperature | 204 - 249 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC G-2163 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Sanren Y3500 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| SuperLite® SL551200-100 (6.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Zhongfa PP GR-30H | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Zhongfa PA66 66G30 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |