RTP 201 TFE 20 SI 2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6rmiMK_RTP-201-TFE-20-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 201 TFE 20 SI 2 is a glass fiber, PTFE, silicone fluid modified nylon 6/6. It provides a unique level of stiffness and wear resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength | 101 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.1 | % | ASTM D638 |
| Flexural Modulus | 3860 | MPa | ASTM D790 |
| Flexural Strength | 139 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 450 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 243 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 227 | °C | ASTM D648 |
| CLTE - Flow | 4.9E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.40 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Specific Gravity, ASTM D-792: 1.36-1.38Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 10mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 274 - 288 | °C | |
| Middle Temperature | 274 - 288 | °C | |
| Front Temperature | 274 - 288 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Soarnol® D2908H4 | Soarus L.L.C. | EVOH | Soarnol® |
| Ultramid® Aqua UV BK20592 | BASF Corporation | Nylon 66 | Ultramid® |
| CP PRYME® Polypropylene PPC100/2I-20M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Durepol® PBT A3 G10 NTLA010 BT309 MSP | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| HiFill® PA6/6 CM16 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |