Trithene® TS 9022
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6rYoa8_Trithene-TS-9022.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®TS 9022 is a low density polyethylene material,. This product is available in Latin America and is processed by film extrusion. Trithene®The main features of TS 9022 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.931 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 14.0 | MPa | ASTM D638 |
| Fracture, molding | 12.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 520 | % | ASTM D638 |
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.12 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 150 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 160 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 380 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 680 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 330 | g | ASTM D1922 |
| TD : 50 µm, blown film | 230 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm, Blown Film) | 90 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 1.8 to 2.6 g/10 minDensity, ASTM D1505: 0.929 to 0.933 g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 - 160 | °C | |
| Cylinder Zone 2 Temp. | 160 - 170 | °C | |
| Cylinder Zone 3 Temp. | 165 - 170 | °C | |
| Adapter Temperature | 165 - 175 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HR2101D | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Color-in™ ABS-M | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | Color-in™ |
| INELEC PEEKCF10HF | Infinity LTL Engineered Compounds | PEEK | INELEC |
| MAJORIS CT273 | AD majoris | PP, Unspecified | MAJORIS |
| POLYfill PPH GF5010 VT2 | Polykemi AB | PP Homopolymer | POLYfill |