LNP™ LUBRICOMP™ ZFG26 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6r4A1o_LNP-LUBRICOMP-ZFG26-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZFG26 is a compound based on PPE+PS resin containing 30% Glass Fiber, 10% Graphite. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound ZFL-4326 Product reorder name: ZFG26 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 | g/cm³ | ASTM D792 |
| -- | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.73 | % | ISO 294-4 |
| Flow : 24 hr | 0.36 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13100 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 110 | MPa | ASTM D638 |
| Yield | 109 | MPa | ISO 527-2 |
| Break | 115 | MPa | ASTM D638 |
| Break | 109 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 1.5 | % | |
| Break | 1.5 | % | |
| Flexural Modulus | |||
| -- | 10500 | MPa | ASTM D790 |
| -- | 10000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 165 | MPa | ASTM D790 |
| -- | 163 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.62 | ||
| vs. Itself - Static | 0.89 | ||
| Wear Factor - Washer | 113 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 2 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.30 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 140 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 135 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® AGF50 BK45 | Ravago Group | Nylon 66 | Ravamid® |
| ATPioneers PP CAP501 | Asia Technology Pioneers Ltd | TPO | ATPioneers PP |
| Dryflex® 4103 | ELASTO | TPE | Dryflex® |
| Dryflex® 602500 A01 | ELASTO | SEBS | Dryflex® |
| Hanwha Total PP FH44 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |