OPTODYNE™ UV-2100
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | OPTODYNE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6nupmc_OPTODYNE-UV-2100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Optodyne UV-2100 is a single component, epoxy-based UV curable adhesive designed for bonding optical connectors, lenses, prisms and other optical components. Its exceptional strength, combined with its unique index matching capability, make the Optodyne Series of adhesives superior in many respects:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | Internal Method | ||
| -- 1 | 1.31 | g/cm³ | |
| -- 2 | 1.38 | g/cm³ | |
| Molding Shrinkage - Flow 3 | 4.0 | % | Internal Method |
| Water Absorption 4(24 hr) | 0.29 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore D) | 80 | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature 6 | 100 | °C | Internal Method |
| Glass Transition Temperature 7 | 129 | °C | Internal Method |
| CLTE - Flow 8 | 1.1E-4 | cm/cm/°C | Internal Method |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Flash Point - Before Cure | 128 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature of Intial Weight Loss - 5% Weight Loss 9 | 305 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 10 | 1.453 | Internal Method | |
| Transmittance 11 | 93.9 | % | Internal Method |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | 290 | cP | Internal Method |
| Note Message | |
|---|---|
| 1 . | Before Cure, 25°C |
| 2 . | After Cure, 25°C |
| 3 . | After Cure |
| 4 . | After Cure |
| 5 . | After Cure |
| 6 . | After Cure |
| 7 . | After Cure |
| 8 . | After Cure |
| 9 . | After Cure |
| 10 . | Before Cure, 25°C |
| 11 . | After Cure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2299 X 108578 A | RTP Company | PEEK | RTP |
| McCann PP M30CHPP10 | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| Silopren® LSR 4630FC | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| SUMILITE® PL-1626 (Machining) | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Ferro PP NPP00GW35HB | Ferro Corporation | PP, Unspecified | Ferro PP |