Hyosung Polyketone M230A Low viscosity grade for high flow injection molding (Natural color) |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (240°C/2.16 kg) | 150 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.0 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.45 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 25 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1270 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 49.0 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 205 | °C | |
| 1.8 MPa, Unannealed | 100 | °C | |
| Melting Temperature | 220 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 9237N | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Huafon JF-A-AH7021 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina IICE PVC COMPOUND 801-28/31-Y-ERYM (*) | Karina Ind. e Com. de Pl谩sticos Ltda | PVC, Unspecified | Karina |
| Pacrel® 5395N | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| Sylvin 9785-82 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |