Latan 2
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6m6ciy_Latan-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyoximethylene (POM). High viscosity. Very good tribological properties. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.1 to 2.3 | % | |
| Flow : 2.00 mm | 2.0 to 2.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2600 | MPa | |
| 60°C | 1500 | MPa | |
| 90°C | 1000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 60.0 | MPa | |
| Yield, 60°C | 45.0 | MPa | |
| Yield, 90°C | 30.0 | MPa | |
| Break, 23°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 10 | % | |
| Break, 23°C | 80 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 95 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 75.0 | °C | |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 175 to 200 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SAP-6318XB35 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |
| Titacon® CW901 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Plaslube® ABS 8004 FR | Techmer Engineered Solutions | ABS | Plaslube® |
| Sylvin 6930X06 Grey 9610 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Versaflex™ CE 3120-80N | PolyOne Corporation | TPE | Versaflex™ |