UBE NYLON 5033 FDX27 is a medium viscosity Polyamide 6/6.6 copolymer. The material is modified for improved slip. It is suitable for cast, air- or water-cooled blown film production. Typical application is for casings and big bags.

General Information
Additive	slip agent
Features	smoothness Workability, good Compliance of Food Exposure Medium viscosity
Uses	Films cast film
Agency Ratings	European food contact, not rated
Forms	Particle
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	0.30	ASTM D1894
With Self-Static	0.30	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD (Cast Film)	400	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, extruded film	24.0	MPa	ASTM D882
Fracture, extruded film	115	MPa	ASTM D882
Tensile Elongation - MD (Fracture, Extruded Film)	650	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	196	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	130		ASTM D523
Haze	3.5	%	ASTM D1003

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Oxygen Permeability, ASTM D3985: 24 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.93Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 85/15Water Vapor Permeability, JIS Z0208: 60 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 12 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Additional Information

The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Oxygen Permeability, ASTM D3985: 24 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.93Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 85/15Water Vapor Permeability, JIS Z0208: 60 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 12 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Resin Grade	Manufacturer	Category	Trademark
RABALON® T331C	Mitsubishi Chemical Performance Polymers, Inc.	TPE	RABALON®
Telcar® TL-8712R	Teknor Apex Company	TPE	Telcar®
DENKA POVAL K-05	Denka Company Limited	PVOH	DENKA POVAL
EVALENE® PP PHJ1201	JG Summit Petrochemical Corporation	PP Homopolymer	EVALENE® PP
LNP™ THERMOCOMP™ RF0029S compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6iNx65_UBE-Nylon-5033-FDX27.pdf
PRICE:	Order Products email sales@su-jiao.com