HAIPLEN H30 G8 BA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6htRYR_HAIPLEN-H30-G8-BA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAIPLEN H30 G8 BA is a Polypropylene Homopolymer (PP Homopolymer) product filled with 40% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.60 to 0.80 | % | |
| Flow | 0.20 to 0.40 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 77.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 6800 | MPa | ISO 178 |
| Flexural Stress 2 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 140 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Pre-heater | 70.0 to 80.0 | °C | |
| Drying Time - Pre-heater | 1.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULABLEND® (PC/ABS) M/MB 6 SF | A. Schulman Europe | PC+ABS | SCHULABLEND® |
| ExxonMobil™ LDPE EVA Copolymers LD 358BW | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Durez® 83537 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| HiFill® PA6 IM 435 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| ISOTHANE® 1075A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |