CYCOLAC™ MG37EPX resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6gmf3E_CYCOLAC-MG37EPX-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS plating grade optimized for a broad processing window for both painted and plated applications. NSF standard 61 compliant (80 sq in/L). |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 6.6 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2480 | MPa | ASTM D638 |
| -- | 2720 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 44.0 | MPa | ASTM D638 |
| Yield | 48.0 | MPa | ISO 527-2/5 |
| Break | 36.4 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 3 | 54 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 2810 | MPa | ASTM D790 |
| -- 5 | 2480 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 73.2 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 90.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 88 | J/m | ASTM D256 |
| 23°C | 250 | J/m | ASTM D256 |
| -40°C 7 | 7.0 | kJ/m² | ISO 180/1A |
| -30°C 8 | 8.2 | kJ/m² | ISO 180/1A |
| 23°C 9 | 23 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 35.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 76.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 82.4 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 1000 sec^-1) | 217 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 216 to 229 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 249 to 268 | °C | |
| Nozzle Temperature | 254 to 279 | °C | |
| Processing (Melt) Temp | 254 to 279 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA CN-L03 PLA Clarifying Agent | Polyvel Inc. | PLA | Polyvel PLA |
| Reslen PPH 40K | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Sindustris ABS LHI221 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Karina BLACK PVC COMPOUND CAK 751-48/1-TEC-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lusin® Clean OH 311 | Chem-Trend L.P. | Unspecified | Lusin® |