Ultraform® N 2320 C BK110
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6g8Eea_Ultraform-N-2320-C-BK110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultraform N 2320 C BK110 is a pigmented black, Electro Statically Dissipative (ESD) POM for injection molding applications. Applications Typical applications include gas filler caps, fuel pump housings/caps, fuel flanges, reservoirs, and rollover valves, where dissipation of electrostatic charge is desired. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 0.500 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 2.3 | % | |
| Flow | 2.3 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 69.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 6.5 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 9.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 170 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound TH3022N | Samyang Corporation | PC | TRIREX® Compound |
| Allen ABS 552/LXS | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Fainplast PVC CKL 93 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| MAJORIS DFR111R | AD majoris | PP, Unspecified | MAJORIS |
| O'Tech OW 939 | O'Tech Corporation | PVC, Unspecified | O'Tech |