APEX® RM 9012
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Teknor Apex Company |
| Trademark: | APEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6g2dTX_APEX-RM-9012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| APEX® RM 9012 is a Rigid Polyvinyl Chloride material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3190 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 43.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus 3 | 2620 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 640 | J/m | ASTM D256 |
| Drop Impact Resistance 4(23°C) | 111 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm) | 70.5 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Procedure A, TUP |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP PSU 1000 | Quadrant Engineering Plastic Products | PSU | Quadrant EPP |
| Miramid® SE40CW | BASF Leuna GmbH | Nylon 66 | Miramid® |
| VESTOSINT® 1161 white | Evonik Industries AG | Nylon 12 | VESTOSINT® |
| Multi-Flex® TPO 2503 S | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| SD POLYCA™ CR3420T | Sumika Styron Polycarbonate Limited | PC+PBT | SD POLYCA™ |