WPP TPO TPO-2563AS UV Black
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP TPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6fGyu7_WPP-TPO-TPO-2563AS-UV-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP TPO TPO-2563AS UV Black is a composite polypropylene product containing 25% mineral fillers. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 14.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 200 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -40°C | 3.5 | kJ/m² | ISO 180 |
| 23°C | 38 | kJ/m² | ISO 180 |
| Instrumented Dart Impact 2 | ASTM D3763 | ||
| -30°C | 22.0 | J | ASTM D3763 |
| 23°C | 18.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 68.0 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 1.5E-4 | cm/cm/°C | ASTM E831 |
| Additional Information |
|---|
| Tensile Strain at Break, ISO 527, 50mm/min: >200% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 87.8 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 210 - 216 | °C | |
| Front Temperature | 216 - 227 | °C | |
| Nozzle Temperature | 210 - 227 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 4.14 - 10.3 | MPa | |
| Holding Pressure | 1.72 - 4.83 | MPa | |
| Back Pressure | 0.517 - 1.03 | MPa | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Speed: 0.25 to 2.5 in/sZone 4 Temperature: 420 to 450°FHot Runner Temperature: 420 to 460°FHydraulic Oil Temperature: 110 to 125°FShot Capacity vs. Barrel Capacity: 2.5 to 4Screw Decompression: 0.1 to 0.25 in |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayblend® T88 GF-20 | Covestro - Polycarbonates | PC+SAN | Bayblend® |
| LAMIGAMID® 100 | Schwartz Technical Plastic | Nylon 6 | LAMIGAMID® |
| LNP™ LUBRICOMP™ Lexan_LF1010 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |
| LUVOCOM® 1850/PL/15/BK | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| KMI PP KM-8216-PP BLK | KMI Group, Inc. | PP, Unspecified | KMI PP |