TES J-50/30/FR
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | TES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6dOqHk_TES-J-50-30-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Molding Parameters: 4 hours recommended for high tensile strength and smooth surface finish, or for vacuum metalizing. The dry temperature at 16 hours is 180°F. For 2-zone machines, the rear temperature is 550-590°F, and the front temperature is 540-560°F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 | % | |
| 6.35 mm | 0.30 | % | |
| Water Absorption (24 hr) | 0.17 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7580 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 114 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8270 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 162 | MPa | ASTM D790 |
| Compressive Strength | 145 | MPa | ASTM D695 |
| Shear Strength | 65.5 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 152 | °C | ASTM D648 |
| CLTE - Flow | 1.4E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.47 mm) | 125 | °C | UL 746 |
| RTI Imp (1.47 mm) | 115 | °C | UL 746 |
| RTI Str (1.47 mm) | 125 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 310 | °C | |
| Front Temperature | 282 to 293 | °C | |
| Nozzle Temperature | 277 to 293 | °C | |
| Processing (Melt) Temp | 282 to 299 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SANTAC® ET-70 | Nippon A&L Inc. | ABS | SANTAC® |
| Boda BDF25P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Hifax CA 1110 G2 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Hanwha Total PE 4142W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| XYLEX™ X7300CL resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |