DOW™ HDPE NG7000
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6bRXhZ_DOW-HDPE-NG7000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ HDPE NG7000 is a High Density Polyethylene Resin material. It is available in Latin America. Important attributes of DOW™ HDPE NG7000 are:
Typical application of DOW™ HDPE NG7000: Food Contact Applications |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.949 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 11 | g/10 min | |
| 190°C/5.0 kg | 0.40 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Film Puncture Resistance (15 µm) | 4.96 | J/cm³ | Internal Method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm | 40.0 | MPa | |
| TD : Yield, 15 µm | 30.0 | MPa | |
| MD : Break, 15 µm | 77.9 | MPa | |
| TD : Break, 15 µm | 42.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 380 | % | |
| TD : Break, 15 µm | 670 | % | |
| Dart Drop Impact (15 µm) | 49 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm | 6.0 | g | |
| TD : 15 µm | 47 | g |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 211 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AESNO MED | Arkema | Nylon 12 | Rilsamid® |
| Moplen EP380S | PolyMirae | PP Copolymer | Moplen |
| UmaPET IT | Ester Industries Ltd. | PET | UmaPET |
| Karina WHITE PVC COMPOUND BR-11 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OP - Acetal C-Acetal 20PTFE | Oxford Polymers | Acetal (POM) Copolymer | OP - Acetal |