Formolene® E927
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6aerAO_Formolene-E927.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Formolene E927 is a high molecular weight grade of HDPE designed for high drawdown to produce thin films with good processing and physical properties. E927 is well balanced in overall physical properties and provides good stiffness for thin gauge film applications. Formolene E927 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. Suggested Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.070 | g/10 min | |
| 190°C/21.6 kg | 12 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 15 µm, Blown Film | 814 | MPa | |
| 1% Secant, TD : 15 µm, Blown Film | 1010 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 15 µm, Blown Film | 57.2 | MPa | |
| TD : Break, 15 µm, Blown Film | 49.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm, Blown Film | 280 | % | |
| TD : Break, 15 µm, Blown Film | 410 | % | |
| Dart Drop Impact (15 µm, Blown Film) | 380 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm, Blown Film | 11 | g | |
| TD : 15 µm, Blown Film | 60 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 131 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REPROCESSED PPH T20-300R | NEXT Specialty Resins, Inc. | PP Homopolymer | NEXT REPROCESSED |
| Nypol® PA A3 G27 NTLA010 NR364 MSM | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Hylon® N2215L | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| IROGRAN® A 95 H 4678 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| OP - PPO PPOX-190-FR | Oxford Polymers | PPE+PS | OP - PPO |