NYCOA Polyamide 2326 UV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6aQiNe_NYCOA-Polyamide-2326-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2326 UV is an impact modified, UV stabilized Nylon 6 resin, which offers outstanding toughness, impact strength and chemical resistance. NYCOA 2326 UV has been specially formulated to give a high degree of impact strength, without the loss of stiffness and rigidity. In addition, this product is stabilized to allow continued exposure to sunlight, and others forms of light. NYCOA 2326 UV processes easily on conventional injection molding and extrusion equipment. Typical applications include clips, fasteners, wiring harnesses, power tool housings, and connectors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 | % | ASTM D955 |
| Transverse flow | 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 75 | % | ASTM D638 |
| Flexural Modulus 3 | 1540 | MPa | ASTM D790 |
| Flexural Strength 4 | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 140 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SYNTECA® 63 | Synthos S.A. | Rubber | SYNTECA® |
| UBESTA 3035UF | UBE America, Inc. | Nylon 12 | UBESTA |
| Nucrel® 0411HS | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| APEX® 80328-Y | Teknor Apex Company | PVC, Flexible | APEX® |
| Sumiliteresin® PR-51732 | SBHPP | Phenolic | Sumiliteresin® |