Mapex AT0320GN
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Mapex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ZqFdK_Mapex-AT0320GN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mapex AT0320 GN PA6.6 is a 15 % glass fiber reinforced impact modified product for injection moulding in natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (1.60 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 4480 | MPa | ISO 178 |
| Flexural Stress | 166 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 245 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 250 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength, ISO 180/1, notch 0.25in: 134 kg cm/cmNotched Izod Impact Strength, ISO 180/1, notch 0.25in, -30°C: 134 kg cm/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 - 300 | °C | |
| Middle Temperature | 250 - 300 | °C | |
| Front Temperature | 250 - 300 | °C | |
| Nozzle Temperature | 290 - 305 | °C | |
| Mold Temperature | 30.0 - 100 | °C | |
| Injection Pressure | 50.0 - 120 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 30.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 0.300 | MPa | |
| Screw Speed | 60 - 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 GB 10 TFE 13 SI2 | RTP Company | Nylon 66 | RTP |
| UBE Polyethylene F522 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Naxel PC502 | Custom Resins Group | PC | Naxel |
| Nycal™ 2155R33T2 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| FHR EPS 54-S7354 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |