Therma-Tech™ TT6600-5004 EI White
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Therma-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ZZpzw_Therma-Tech-TT6600-5004-EI-White.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.92 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 15500 | MPa | ISO 527 |
| Tensile Strength 2(Break, 23°C) | 75.0 | MPa | ISO 527 |
| Tensile Elongation 3(Break, 23°C) | 0.50 to 1.0 | % | ISO 527 |
| Flexural Modulus 4(23°C) | 12500 | MPa | ISO 178 |
| Flexural Strength 5(23°C) | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 9.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | |||
| 23°C 6 | 1.1 to 1.3 | W/m/K | ASTM E1461 |
| 23°C 7 | 1.2 | W/m/K | |
| 23°C 8 | 2.7 to 3.2 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 80.0 to 105 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 1.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 10 mm/min |
| 5 . | 10 mm/min |
| 6 . | Through-Plane |
| 7 . | Through Plane with Modified Transient Plane Source |
| 8 . | In-Plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4807 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| S&E Wire & Cable GA-509OR | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| KOPA® KN332G30V0BK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LUVOCOM® 1105-8914 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| TechnoFiber Performance PP LGF 60-10-02 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber Performance |