Braskem PE ML3601U
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6YEa9T_Braskem-PE-ML3601U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The resin ML3601U is a Linear Low Density Polyethylene, 1-hexene copolymer, indicated for rotational molding. It presents excellent environmental stress cracking resistance and high impact strength. This resin is ideally suited for applications that require a higher mechanical performance and coog chemical resistance. Applications: Large tanks for water and chemical products storage, underground tanks, septic tanks and manholes. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.3 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 2.00mm, 10% Igepal, molded, F50 | 145 | hr | ASTM D1693 |
| 50°C, 2.00mm, 100% Igepal, molded, F50 | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 21.0 | MPa | ASTM D638 |
| Fracture, molding | 30.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 14 | % | ASTM D638 |
| Fracture, molding | > 1000 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 760 | MPa | ASTM D790 |
| Fundamentals of Hydrostatic Design | 8.62 | MPa | ASTM D2837 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time | > 100 | min | ASTM D3895 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | ARM | ||
| -40°C, 3.17mm, rotational molding | 82 | J | ARM |
| -40°C, 6.34mm, rotational molding | 228 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, molded | 60.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, molded | 41.0 | °C | ASTM D648 |
| Peak Melting Temperature | 127 | °C | ASTM D3418 |
| Additional Information |
|---|
| Rotomolding Oven Temperature: 250 to 350°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800U (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| SEETEC PP M1600 | LG Chem Ltd. | PP Impact Copolymer | SEETEC PP |
| Sindustris PP HM5205 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sylvin 5150-60 Yellow 4124 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SD POLYCA™ LD2050-AEA02 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |