Bergamid™ B70 GK/MI15 black
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6XHLM7_Bergamid-B70-GK-MI15-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6016158 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 2(23°C, 4.00 mm, Injection Molded) | 1.5 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 4400 | MPa | ISO 527-2/1 |
| Tensile Strength 3(23°C, 4.00 mm, Injection Molded) | 73.0 | MPa | ISO 527 |
| Tensile Strain (Break, 23°C, 4.00 mm, Injection Molded) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 50 | kJ/m² | ISO 179 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm, ALL) | HB | Internal Method | |
| Glow Wire Flammability Index (3.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| 2 . | Bergmann Method |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 LF TFE 5 | RTP Company | PEEK | RTP |
| RAMOFIN PPH308G6 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| Ferro PP NPP00GW35HB | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hifax TRS 372P | LyondellBasell Industries | PP Copolymer | Hifax |
| Polygen SG8L | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |