Axiall PVC SP-5034
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Axiall PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6XGRoq_Axiall-PVC-SP-5034.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Georgia Gulf SP-5034 is a rigid vinyl injection molding compound designed for fittings and parts of similar configuration where maximum burst strength is required. Georgia Gulf 5034 is ideally suited for large diameter fittings. Georgia Gulf 5034 is listed with NSF under Standard 14, and meets Standard 61 health effects requirements. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| PVC Cell Classification | 12454-B | ASTM D1784 | |
| Flow Ratio (199 to 204°C) | 120 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.18 mm | 37 | J/m | |
| 23°C, 3.18 mm | 80 | J/m | |
| Gardner Impact (23°C) | 36.2 | J | ASTM D3029 |
| Drop Impact Resistance (23°C) | 114 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 74.0 | °C | |
| 1.8 MPa, Unannealed | 70.0 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 38 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Shot Size | 35 to 75 | % | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 163 | °C | |
| Middle Temperature | 174 to 191 | °C | |
| Front Temperature | 182 to 193 | °C | |
| Nozzle Temperature | 177 to 193 | °C | |
| Processing (Melt) Temp | 202 to 210 | °C | |
| Mold Temperature | 15.6 to 48.9 | °C | |
| Injection Pressure | 82.7 to 138 | MPa | |
| Holding Pressure | 48.3 to 82.7 | MPa | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 25 to 80 | rpm | |
| Clamp Tonnage | 3.4 | kN/cm² | |
| Screw L/D Ratio | 16.0:1.0 to 24.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AF30BK6030 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| BJB Polyurethane TC-8764 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| HiFill FR® PP GF10 FR BK | Techmer Engineered Solutions | PP, Unspecified | HiFill FR® |
| LIHAN® A102 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| NORYL GTX™ GTX830 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |