| PC/ABS-blend Glass-reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 48.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4200 | MPa | ISO 178 |
| Flexural Stress | 84.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 109 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 116 | °C | ISO 306/A50 |
| -- | 105 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITAL® LZ | Nytef Plastics, Ltd. | Acetal (POM) Copolymer | UNITAL® |
| ELASTOSIL® LR 3844/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| ICORENE® 9035 | ICO Polymers APAC, A Division of A. Schulman | LMDPE | ICORENE® |
| LEXAN™ 940 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| PLUSTEK PA840G3 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |