Ebalta AH 120 / TG
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6WhB3h_Ebalta-AH-120-TG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 84 to 88 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2900 to 3400 | MPa | ISO 178 |
| Flexural Stress | 110 to 130 | MPa | ISO 178 |
| Compressive Stress | 95.0 to 115 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 41 to 51 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 to 96.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 22 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time | |||
| 60°C | 6.0 to 8.0 | hr | |
| 90°C | 3.0 to 5.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.10 to 1.14 | g/cm³ | |
| Viscosity (25°C) | 0.62 to 0.82 | Pa·s | |
| Curing Time (20°C) | 10 to 12 | hr | |
| Pot Life 1(20°C) | 35 to 40 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS HF-3 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Titanvene™ HD5120GB-B | PT. TITAN Petrokimia Nusantara | HDPE | Titanvene™ |
| Elastollan® C 85 A HPM | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Globalprene® 3566 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| POLYAXIS® LP 8000 | A. Schulman Inc. | mHDPE | POLYAXIS® |