PTS PCA-3013
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | PTS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6Rd6e7_PTS-PCA-3013.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PTS PCA-3013 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 150 | % | ASTM D1708 |
| Flexural Modulus (3.17 mm) | 1830 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 63.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 238 to 249 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 252 to 274 | °C | |
| Nozzle Temperature | 252 to 263 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Back Pressure | 1.72 to 3.45 | MPa | |
| Screw Speed | 25 to 50 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPTON™ 1001 | Kuraray Co., Ltd. | SEP | SEPTON™ |
| Sylvin 5175-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® OM-10176 | Teknor Apex Company | TPE | Monprene® |
| Andur AL 90 AP/Curene® 89LC | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Sylvin 4280-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |